Ehdotuksen tiedot

Tunnus:prEN ISO 18610
Julkaisija:CEN
Komitea:CEN/TC 184
Komitean nimi:Advanced technical ceramics
Lausuntokierros alkanut:2020-08-30
Lausuntopyynnön määräaika:2020-10-29
Vastuuhenkilö:frans.nilsen(at)metsta.fi
Ehdotuksen soveltamisala:ISO 18610:2016 specifies an ultrasonic method to determine the components of the elasticity tensor of ceramic matrix composite materials at room temperature. Young's moduli shear moduli and Poisson coefficients, can be determined from the components of the elasticity tensor.It applies to ceramic matrix composites with a continuous fibre reinforcement: unidirectional (1D), bidirectional (2D), and tridirectional (×D, with 2 < × = 3) which have at least orthotropic symmetry, and whose material symmetry axes are known.This method is applicable only when the ultrasonic wavelength used is larger than the thickness of the representative elementary volume, thus imposing an upper limit to the frequency range of the transducers used.

Rekisteröidyttyäsi Lausuntopyyntöpalvelun käyttäjäksi voit lukea standardiehdotuksia ja kommentoida niiden sisältöä.

Kun haluat kommentoida lukemaasi tekstiä, valitse Lue ehdotus ja anna muutosehdotuksesi kohdassa Jätä kommentti.

Voit myös kertoa mielipiteesi standardiehdotuksesta kokonaisuutena. Ota kantaa siihen, hyväksytkö standardiehdotuksen vahvistamisen standardiksi.